C15E, CK15, 1.1141, C15, 15 - carbon steel acc. to ISO 683-3, PN-H-84019, GOST 1050.
Table of content:
| Standard | Grade | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Chemical composition % | |||||||||||||||
| C: | Si: | Mn: | P: | S: | |||||||||||
| PN | 15 | ||||||||||||||
| 0.12-0.19 | 0.15-0.40 | 0.35-0.65 | <0.04 | <0.04 | |||||||||||
| GOST | 15 | ||||||||||||||
| 0.12-0.19 | 0.17-0.37 | 0.35-0.55 | <0.03 | <0.035 | |||||||||||
| DIN/EN | C15E / Ck15 / 1.1141 | ||||||||||||||
| 0.12-0.18 | <0.4 | 0.3-0.6 | <0.035 | <0.035 | |||||||||||
| EN | C15R / 1.0401 | ||||||||||||||
| 0.12-0.18 | <0.4 | 0.3-0.6 | <0.035 | 0.02-0.04 | |||||||||||
| NF | XC15 | ||||||||||||||
| 0.12-0.18 | <0.35 | 0.3-0.7 | <0.04 | <0.035 | |||||||||||
| STAS | OLC15 | ||||||||||||||
| 0.12-0.18 | 0.17-0.37 | 0.35-0.65 | <0.04 | <0.045 | |||||||||||
| BS | 080A15 | ||||||||||||||
| 0.13-0.18 | - | 0.7-0.9 | <0.035 | <0.035 | |||||||||||
| BS | 080M15 | ||||||||||||||
| 0.12-0.18 | - | 0.6-1.0 | <0.035 | 0.02-0.04 | |||||||||||
| ASTM | AISI 1015 / UNS G10150 | ||||||||||||||
| 0.13-0.18 | - | 0.3-0.6 | <0.04 | <0.05 | |||||||||||
C15E, CK15, 1.1141, C15, gat. 15 - description
Common unalloyed steel for carburizing and hardening. A bit stronger than C10E and a bit weaker than C20E.
In carburized and quenched condition it is used for light-duty parts like pivots, axles, shafts, levers, pins, bolts, nuts.
In normalized condition it is used mainly for fasteners.
Physical and mechanical properties
- General properties according to ISO 683-3:
- In delivery condition (+A): <143 HB
- In normalised condition (+N): 95-150 HB
- Bright bars in soft annealed and cold drawn condition +A,+C:
- Diameters: 5-10 mm - <238 HBW
- Diameters: 10-16 mm - <231 HBW
- Diameters: 16-40 mm - <216 HBW
- Diameters: 40-63 mm - <198 HBW
- Diameters: 63-100 mm - <178 HBW
- Bright bars in cold drawn condition +C:
- Diameters: 5-10 mm
- Tensile strength Rm: 500-800 MPa
- Yield strength Re: >380 MPa
- Elongation A: >7 %
- Diameters: 10-16 mm
- Rm: 480-780 MPa
- Re: >480 MPa
- A: >8 %
- Diameters: 16-40 mm
- Rm: 430-730 MPa
- Re: >280 MPa
- A: >9 %
- Diameters: 40-63 mm
- Rm: 380-670 MPa
- Re: >240 MPa
- A: >9 %
- Diameters: 63-100 mm
- Rm: 340-600 MPa
- Re: >215 MPa
- A: >12 %
- Diameters: 5-10 mm
- Bright bars:
- in rolled and peeled condition (+SH): 98-178 HBW
- in soft annealed and peeled condition (+A+SH): <131 HBW
- Steel strip in cold-rolled condition +CR:
- Rm: <870 MPa
- <260 HV
- Steel strip in soft annealed and cold-drawn condition +A; +LC:
- Rm: <450 MPa
- HV: <140
Heat treatment and working
Recommended working and heat treatment parameters for C15E alloy:
- Soft annealing: 650-700 °C
- Normalising: 890-920 °C
We deliver this steel alloy as:
- Colddraw, hot-rolled and forged bars
- Sheets and plates
Replacements, equivalents and other designations:
C15E, 15, 2C15, 3C15, C15D, C15D2, C15R, C16E, C16R, XC12, XC15, XC18, Ck15, 080A15, 080M15, CE15E4, SHC15, SM15C, OLC15, AISI 1015, UNS G10150, 505, 1.1141, 1141.0 BOHLER G, BGH 1141, Buderus Ck15, CARBODUR C15E, Ck15k, DIRO-Ck 15, Eschmann Ck 15, Klockner Ck 15, TS Ck 15, Almenit 1141, BOHLER E920, C15E, DE1141, EW Ck15, IS1141, OVAKO 017A, UHB Ck15